Keywords:Glass durability
,
Iron slag
,
SEM
,
Silicate glass
,
Corrosion
,
Corrosion resistance
,
Durability
,
Electromagnetic wave absorption
,
Energy dispersive X ray analysis
,
Fourier transform infrared spectroscopy
,
Fused silica
,
Iron
,
Leaching
,
Light absorption
,
Lime
,
Nitric acid
,
Scanning electron microscopy
,
Silicates
,
Slags
,
X ray analysis
,
Chemical durability
,
Energy dispersive x-ray analysis (EDX)
,
Glass compositions
,
Glass durability
,
Iron slags
,
Silicate glass
,
Soda lime silicate glass
,
Structural concept
,
Glass
Abstract:
Soda lime silicate glasses containing different amounts of iron slag 30 % were prepared. The chemical durability of the prepared glasses was examined by immersion in HCl or HNO3 solutions at room temperature. The results show that the glass durability increases with increasing the amount of slag in the glass composition to a certain amount, then followed by a decrease in the glass durability. Various mechanisms of corrosion and the role of the mobility of cations and their leaching into solution, also the effect of time of leaching are discussed. The densities of all glass compositions were measured. The quantitative analysis obtained from infrared absorption spectra in the range of (400 4000) cm?1 in relation to the effect of corrosion on the absorption spectra has been studied in terms of structural concepts. The topography of the glass surfaces was observed by scanning electron microscopy (SEM). The concentration percentage of the ions present on the glass surface was determined by Energy Dispersive X-ray analysis (EDX). 2015, Springer Science+Business Media Dordrecht.
Abou Hussein E.M.; Abd Elaziz T.D.; El-Alaily N.A.(Springer New York LLC, 2019)
Lithium bismuth silicate glasses with the composition of; 68% SiO2, 20% Bi2O3, 8% Li2O3, 4% Na2O doped with either 2% PbO, BaO or SrO (all in wt%) were studied to investigate some of their optical and electrical properties ...
Preparing glass to be used as a radioactive waste immobilizer from municipal waste is the aim of this paper. Up to 90 wt% of municipal waste was obtained by burning the raw waste at 700 C for 5 h; this were successfully ...
Khalil M.M.; Abdelrahman M.H.; El-Mallah S.(Wroclaw Medical University, 2019)
Background. Endodontic sealers are essential for sealing gutta-percha to the dentin walls. They help to ensure that the canal remains free of microorganisms which might lead to infection. In order to perform their intended ...